针对双向拉伸聚丙烯薄膜(BOPP)包装材料,制备低热封丙烯酸乳液涂层材料.通过考察聚合工艺,调节单体比例、乳化剂、引发剂及其用量,测定乳液性能.研究结果表明:以十二烷基硫酸钠(K12)作为乳化剂,其适中的质量分数为0.5%,以质量分数为0.5%的过硫酸铵作为引发剂,软硬单体按质量比为1∶1混合,进一步加入质量分数为2%的功能性单体丙烯酸(AA),所制备的乳液稳定性较好,成膜性优异,热封强度达到2.64 N/cm,大大超过现有市场产品的性能.
Abstract：The acylic emulsion with low heat sealing performance is synthesized for double oriented polypropylene film(BOPP) packaging materials.The effect of polymerization process,ration of monomer content,emulsifier,initiator and its content on emulsion performance are taken into account.The results are showed that: the sodium lauryl sulfate(K12) with a total mass account of 0.3% is properly used as emulsifier,ammonium persulfate with 0.5% content is used as initiator;The appropriate ration of hard and soft monomers is 1:1.By adding 2% acrylic acid(AA),the emulsion enjoys a good adhesion with BOPP,while the peel strength reached 2.64 N/cm.
[1]Ravindra U,Raireselise D N,Ntino C,et al.Synthesis ofAcrylic polyurethane Hybrid Latexes by Mini emulsionPolymerization and T heir Pressure sensitive Adhesive Ap-plications[J].Macromolecules,2011,44(8):2632-2642.
[2]陈小锋.水性复膜胶发展的春天来临[J].新材料产业,2009(6):38-40.
[3]黄增芳,瞿晓岳,谢辉,等.聚丙烯酸酯苯乙烯/纳米SiO2复膜胶的制备及性能研究[J].包装工程,2010,31(21):7-10.
[4]Zhou Changlin,Che Rongsheng,Zhong Ling,et al.Effectof particle structure on the peel strength and heat resistanceproperties of vinyl acetate/acrylate latexes laminating adhe-sives[J].Journal of Applied,2009,35(6):12-14.
[5]Tang Jianxin,Chen Hong,Nie Libo,et al.Synthesis of selfcross linking water soluble acrylic resin and development ofte extra color super impose printing inks[J].Journal ofSoutheast University:Natural Science Editon,2003,33(1):68-71.
[6]Custódio J E P,Eusébio M I.Waterborne acrylic varnishesdurability on wood surfaces for exterior exposure[J].Progressin Organic Coatings,2006,56(1):59-67.
[7]谭文丽,王树根,田秀枝,等.核壳型有机硅改性丙烯酸酯涂料印花黏合剂[J].印染,2008,6(12):5-8.
[8]伊峻.罗门哈斯在中国推广水性复合薄膜胶黏剂[J].薄膜材料及应用,1996,14(4):9-13.
[9]王杨勇,胡剑青,郑智贤,等.软包装用耐水丙烯酸酯胶黏剂乳液的合成研究[J].包装工程,2011(8):74-78.
[10]康凯,阐成友,杜奕,等.MMA/EA/AA无皂乳液聚合中粒径及粒径分布的控制[J].高分子学报,2004,8(4):580-584.
[11]吕晶.低温黏合剂的研制及应用[J].印染助剂,2001,18(6):11-13.
[12]Warson H.The application of synthetic resin emulsion[J].Synthetic Resin Emulsion,2008,93(1):87-93.
[13]Lee C-F.The characteristic properties of poly(methylmethacrylate)/polystyrene core-shell composite polymer latex[J].Soil Biology&Biochemistry,2001,33(5):907-912.
[14]王维盈,凌爱莲,桑鸿勋,等.丙烯酸酯乳液影响因素的研究[J].北京工业大学学报,2002,28(2):150-154.
[15]陶子斌.丙烯酸生产与应用技术[J].丙烯酸合成及应用,1997,25(2):33-38.
基本信息:
DOI：
中图分类号:TQ316.33
引用信息:
[1]刘桃凤,吴绥菊,朱鹏等.低热封包装材料用丙烯酸酯乳液的合成研究[J],2012,11(02):47-51.
基金信息:
江苏省高校自然科学基金项目(09KJD430008);; 南通大学引进人才启动费项目(09R03);; 南通市应用研究计划项目(BK2011033)