采用溶胶凝胶法制备了不同掺杂量的纳米Cu2+/TiO2复合材料,研究其无紫外光照射时的抗菌性能.结果表明,n(Cu):n(Ti)=1:50～1:10时,纳米Cu2+/TiO2复合材料无需紫外光照射均具有较强的抗菌性能,对大肠杆菌和金黄葡萄球菌产生透明抑菌圈,直径为6～26 mm.适量掺杂时以催化机理杀菌,过量掺杂时以溶出机理杀菌.
Abstract：Nanometer Cu2+/TiO2 composite materials doped with different content of Cu2+ were prepared and their antibacterial activity without UV irradiation was studied.The test results show that the composite materials have excellent antibacterial activity without UV irradiation when n(Cu)∶n(Ti) is 1∶50 to 1∶10.They have clear antibacterial circle of 626 mm toward E.coli and S.aureus.Their antibacterial mechanism is photocatalysis when proper amount of Cu2+ doped and contacting mechanism when excessive Cu2+ added.
[1]黄岳元,米钰,郭人民,等.TiO2/Ag纳米抗菌材料[J].西北大学学报,2003(10):566-568.
[2]迟广俊,姚素薇,范君,等.Ni/TiO2复合镀层光催化抗菌性能的研究[J].材料科学与工艺,2004,12(1):52-56.
[3]叶瑛,周玉航,夏枚生.载铜蒙脱石及其抗菌机理讨论[J].无机材料学报,2003,3(18):569-574.
[4]蒋亚,刘雪峰,涂铭旌.纳米级介孔复合体的制备及其抗菌性能评价[J].化工新型材料,2003,3:35-36.
[5]汤斌,张庆庆.光析出钛负载银膜的制备及其光催化性能[J].感光科学与技术,2003,5(21):328-333.
[6]刘守新,孙陈林.Ag改性提高TiO2对Cr(VI)的光催化还原活性机理[J].物理化学学报,2004,20(4):355-359.
[7]鞠剑峰,李澄俊,徐铭,等.纳米TiO2复合材料的制备及其抗菌性能研究[J].精细化工,2003,11:645-647.
[8]鞠剑峰,李澄俊,徐铭.纳米Ag/TiO2复合材料的抗菌性能[J].精细化工,2005,1:59-61.
[9]徐瑛,杨增新,李志华,等.二氧化钛复合微粉的抗菌性能研究[J].功能材料.2002,33(6):682-683.
[10]鞠剑峰,施磊,李澄俊,等.纳米TiO2-WO3的制备及对甲醛的光催化降解[J].精细化工,2004,21(3):181-184.
基本信息:
DOI：
中图分类号:R318.08
引用信息:
[1]胡啸林,鞠剑峰.纳米Cu~(2+)/TiO_2复合材料的抗菌性能研究[J].南通大学学报(自然科学版),2007,No.21(02):34-37.
基金信息:
江苏省教育厅指导项目(04KJD540139)